PLA+Special material for biodegradable straw produced by talc powder X905/X908/X909
2024.08.19Visits:442
Product introduction:
PLA+Special material for biodegradable straw produced by talc powder X905/X908/X909
It is a new fully degradable composite made of PLA and PBS through special process. The material can be completely degradable, heat-resistant, odorless and has good toughness; Meet food grade requirements; Suitable for straw, disposable lunch box, etc.
|
model |
X905 |
X908 |
X909 |
|
Main components |
PLA+PBAT+Talc powder |
PLA+PBS+Talc powder |
PLA+PBS+Talc powder |
|
Exterior |
White particles |
White particles |
White particles |
|
Moisture |
≤0.15% |
≤0.15% |
≤0.15% |
|
Density(g/cm3) |
1.38 |
1.25 |
1.25 |
|
Dissolving finger（g/10min）2.16KG |
3-5 |
3-5 |
3-5 |
|
Thermal deformation temperature（0.45MP） |
50℃ |
80℃ |
90℃ |
|
Bending strength（10mm/min） |
44MP |
40MP |
40MP |
|
Bending modulus（10mm/min） |
820MP |
820MP |
800MP |
Packaging and storage:
1*25±0.3kg paper plastic composite bag + lined bag: the product is stored in a dry and ventilated indoor environment with an ambient temperature ≤ 35 ℃, and the storage life is 1 year under the condition that the internal and external packaging are not damaged. When the moisture content is ≥ 500ppm, it is recommended to dry at 80 ℃ for 4 hours before use.